Bioengineered and Biocompatible Zirconia based Ceramics for Tissue Engineering Applications
G. Sankar1, S. Meenaloshini2, R. Dinesh3
1G. Sankar, Department of Mechanical Engineering, University Tenaga Nasional, Kuala Lumpur, Malaysia.
2S. Meenaloshini, Department of Mechanical Engineering, University Tenaga Nasional, Kuala Lumpur, Malaysia.
3R. Dinesh, Department of Mechanical Engineering, University Tenaga Nasional, Kuala Lumpur, Malaysia.
Manuscript received on 04 May 2019 | Revised Manuscript received on 09 May 2019 | Manuscript Published on 13 May 2019 | PP: 342-345 | Volume-8 Issue-7S May 2019 | Retrieval Number: G10610587S19/19©BEIESP
Open Access | Editorial and Publishing Policies | Cite | Mendeley | Indexing and Abstracting
© The Authors. Blue Eyes Intelligence Engineering and Sciences Publication (BEIESP). This is an open-access article under the CC-BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/)
Abstract: This research work explains the densification behavior, mechanical properties, and microstructure of high-purity titanium oxide (TiO2 ) and tricalcium phosphate (TCP)-doped Y-TZP where different weight percentage of TiO2 varied from 0 to 10wt% and a fixed percentage of 15wt% for tricalcium phosphate were used in this research work. The preparation of the samples was done by uniaxially pressing the samples at 200MPa into circular discs and rectangular bars and pressureless-sintered at temperatures ranging between 1200˚C to 1400˚C for 90 minutes holding time. The microstructure of the samples was characterized using the scanning electron microscope (SEM). The obtained results were analyzed for mechanical properties i.e bulk density, compressive strength, and Vickers hardness respectively. The results had shown significant improvement in terms of mechanical properties with the addition of dopants to the pure Y-TZP powder. In addition to that, the dopants have reinforced and toughened the samples. The results obtained for the mechanical properties of the TiO2 and TCP-doped Y-TZP ceramics were 4.89Mgm-3 and 10.67GPa for density, and Vickers hardness, respectively, for the composition of 10wt% TiO2 /15wt% TCP and 75wt% ZrO3 sintered at 1400˚C with 90 minutes holding time.
Keywords: Titanium Oxide, Tricalcium Phosphate, Zirconia Mechanical Properties, Microstructure.